| CuNi1Si (CW109C) |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| 年级： | CuNi1Si |
|
|
|
|
|
| 数量： | CW109C |
|
|
|
|
|
| 分类： | 低合金铜合金 |
|
|
|
|
|
| 密度 | 8.8 克/厘米? |
|
|
|
|
|
| 标准： | EN 12163: 1998 铜和铜合金。一般用途杆 |
|
|
|
|
|
| EN 12166: 1998 铜和铜合金。一般用途电线 |
|
|
|
|
|
| EN 12167: 1998 铜和铜合金。一般用途的型材和矩形条 |
|
|
|
|
|
| EN 12165: 1998 铜和铜合金。锻造和未锻造锻料 |
|
|
|
|
|
| EN 12420: 1999 铜和铜合金。锻件 |
|
|
|
|
|
| 化学成分% CuNi1Si 级 (CW109C) |
|
|
|
|
|
|
| 铁 | 四 | 锰 | 镍 | 铅 | 别人 | - |
| 0。2 | 0.4-0。7 | 0。1 | 1-1。6 | 0.02 | 总0。3 | 铜-余数 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| CuNi1Si 级 (CW109C) 的力学性能 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| Rm -拉伸强度 (MPa) (R240) | 240 |
|
|
|
|
|
|
|
|
|
|
|
|
| Rm -拉伸强度 (MPa) (R410) | 410 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| Rp0.2 0.2% 证明强度 (MPa) (R240) | 90 |
|
|
|
|
|
|
|
|
|
|
|
|
| Rp0.2 0.2% 证明强度 (MPa) (R410) | 320 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| 断裂伸长率 (%)(R240) | 35 |
|
|
|
|
|
|
|
|
|
|
|
|
| A - Min. elongation at fracture (%) (R410) | 9 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| 布氏硬度 (HB): (H050) | 50-75 |
|
|
|
|
|
| 布氏硬度 (HB): (H105) | 105-150 |
|
|
|
|
|
|
|
|
|
|
|
|