CuSn11P-B (CB481K) |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
年级: | CuSn11P-B |
|
|
|
|
|
|
|
|
|
|
数量: | CB481K |
|
|
|
|
|
|
|
|
|
|
分类: | 铜锡合金 |
|
|
|
|
|
|
|
|
|
|
标准: | EN 1982: 2008 铜和铜合金。钢锭和铸件 |
|
|
|
|
|
|
|
|
|
|
化学成分% CuSn11P-B 级 (CB481K) |
|
|
|
|
|
|
|
|
|
|
|
将后缀 B 添加到***中以钢锭的形式识别材料 |
|
|
|
|
|
|
|
|
|
|
|
铁 | 四 | 锰 | 镍 | P | 秒 | 铝 | 铜 | 铅 | 锌 | 某人 | 锡 |
0。1 | 0.01 | 0.05 | 0。1 | 0.6-1 | 0.05 | 0.01 | 87-89。3 | 0.25 | 0.05 | 0.05 | 10.2-11。5 |
CuSn11P-B 级 (CB481K) 的力学性能 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rm -拉伸强度 (MPa) (GS) | 250 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rm -拉伸强度 (MPa) (GM) | 310 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rm -拉伸强度 (MPa) (GC) | 350 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rm -拉伸强度 (MPa) (广州) | 330 |
|
|
|
|
|
|
|
|
|
|
Rp0.2 0.2% 证明强度 (MPa) (GS) | 130 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rp0.2 0.2% 证明强度 (MPa) (GM) | 170 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rp0.2 0.2% 证明强度 (MPa) (GC) | 170 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rp0.2 0.2% 证明强度 (MPa) (广州) | 170 |
|
|
|
|
|
|
|
|
|
|
断裂伸长率 (%)GS | 5 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
断裂伸长率 (%)通用汽车 | 2 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
断裂伸长率 (%)GC | 5 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
断裂伸长率 (%)GZ | 4 |
|
|
|
|
|
|
|
|
|
|
布氏硬度 (HBW): (GS) | 60 |
|
|
|
|
|
|
|
|
|
|
布氏硬度 (HBW): (GM) 或 (GC) 或 (广州) | 85 |
|
|
|
|
|
|
|
|
|
|